Industrial Threaded Graphite Electrodes (UHP Grade) with Nipples
Raw Materials
Petroleum coke, needle coke, coal tar pitch
Production Process
Calcination → Compounding → Kneading → Pressing → Baking → Impregnation → Graphitization → Machining
Grades
RP / HP / UHP
Key Features
Low resistivity
High electrical conductivity
Low ash content
Compact and uniform structure
Excellent oxidation resistance
High mechanical strength
Applications
Used in LF and EAF for the steel-making industry, non-ferrous industry, silicon and phosphorus industries
The best conductive material for electric arc furnaces and smelting furnaces
Used in closed arc and resistance furnaces
For the production of graphite shaped products, such as crucibles, boats, heating elements and other graphite components
Номинальный диаметр | Фактический диаметр | Length (mm) | Допуск | ||||
MM | Inch | Poppy | Mines | The Black Part Min Size | Длина | Short Length | |
75 | 3 | 78 | 73 | 72 | 1400/1600 | ± 100 | -275 |
100 | 4 | 103 | 98 | 97 | 1400/1600 | ||
130 | 5 | 132 | 127 | 126 | 1400 | ||
150 | 6 | 154 | 149 | 146 | 1400/1600/1800 | ||
175 | 7 | 180 | 174 | 172 | 1400/1600 | ||
200 | 8 | 205 | 200 | 197 | 1600/1800 | ||
225 | 9 | 230 | 225 | 222 | 1600/1800 | ||
250 | 10 | 255 | 251 | 248 | 1600/1800 | ||
300 | 12 | 307 | 302 | 299 | 1600/1800/2000 | ||
350 | 14 | 357 | 352 | 349 | 1600/1800/2000 | ||
400 | 16 | 409 | 403 | 400 | 1600/1800/2000/2200 | ||
450 | 18 | 460 | 454 | 451 | 1600/1800/2000/2200 | ||
500 | 20 | 511 | 505 | 502 | 1600/1800/2000/2200 | ||
550 | 22 | 562 | 556 | 553 | 1800/2000/2200/2400 | ||
600 | 24 | 613 | 607 | 604 | 2000/2200/2400/2700 | ||
650 | 26 | 663 | 659 | 656 | 2000/2200/2400/2700 | ||
700 | 28 | 714 | 710 | 707 | 2000/2200/2400/2700 | ||
Technical Characteristics of Graphite Electrode RP, HP, UHP
Элемент | Единица | Графитовый электрод | ||||
РП | HP | Сверхвысокотемпературный | ||||
φ300-φ800mm | φ300-φ800mm | φ300-φ500mm | φ550-φ800mm | |||
Typical Value | Typical Value | Typical Value | Typical Value | |||
Сопротивление | Электрод | μΩm | 7.0-10.0 | 5.8-6.6 | 4.5-5.8 | 4.6-5.8 |
Сосок | 4.0-4.5 | 3.5-4.0 | 3.5-4.0 | 3.5-4.0 | ||
Модуль разрыва | Электрод | Мпа | 8.0-10.0 | 10.0-13.0 | 10.0-14.0 | 10.0-14.0 |
Сосок | 19.0-22.0 | 20.0-23.0 | 20.0-24.0 | 22.0-26.0 | ||
Модуль Юнга | Электрод | ГПа | 7.0-9.3 | 8.0-12.0 | 9.0-13.0 | 10.0-14.0 |
Сосок | 12.0-14.0 | 12.0-14.0 | 15.0-18.0 | 16.0-19.0 | ||
Объемная плотность | Электрод | g/cm3 | 1.53-1.56 | 1.64-1.68 | 1.68-1.74 | 1.70-1.74 |
Сосок | 1.70-1.74 | 1.75-1.80 | 1.78-1.82 | 1.80-1.84 | ||
CTE (100-600ºC) | Электрод | 10-6/ºC | 2.2-2.6 | 1.6-1.9 | 1.1-1.4 | 1.1-1.4 |
Сосок | 2.0-2.5 | 1.1-1.4 | 0.9-1.2 | 0.9-1.2 | ||
Пепел | % | 0.5 | 0.5 | 0.5 | 0.5 | |